Abrasion Resistance Alumina Refractory Bricks For Industrial Furnace

Product Details:
Place of Origin: China
Brand Name: XinYu
Certification: ISO9001
Model Number: XY-A75
Payment & Shipping Terms:
Minimum Order Quantity: 25Tons
Price: USD110~USD550/Ton
Packaging Details: wooden pallet with paper each layer, wrapped with thick paper and PVC film outside.
Delivery Time: 5-8days
Payment Terms: Western Union, T/T, L/C, D/A, D/P
Supply Ability: 500Tons/month

Detail Information

Shape: Brick,Block,customized Material: Alumina Block,calcined Bauxite
Refractoriness (degree): Common (1580°< Refractoriness< 1770°) Application: Industrial Furnaces,Metallurgy,Nonferrous Metal Furnace
Color: Yellow Al2o3 Content (%): 48%-85%
High Light:

high alumina fire bricks


fire clay bricks

Product Description

High alumina refractory fire bricks with resistance to abrasion for industrial furnace blast furnace


Category of Refractory Brick/Fire Brick:
a) According the made method, it can be divided into burnt brick, unburned brick, and electric smelting brick.
b) According the shape and size, it can be divided into standard brick, general brick and abnormal shape brick.
c) According the content of the Al2O3, it can be divided into fire clay brick and high alumina brick.

Production process:
The production process of High Alumina Bricks can be divided into as following process:
Raw material mixing, molding, sintering, selection, packing, delivery.
1) Generally, High Alumina brick was molded by dry pressing.
2) By means of mixing the material uniformity in proportion and ageing mixture some time. Then, pour some powders into the mold and dry pressing.
3) After dry pressing, the adobe needs to be pushed in the drying kiln to stove or stay in the air to dry. This progress will need about 3-5 days.
4) After this progress, then push the adobe into the tunnel furnace or shuttle kiln to burn around 1300C. This progress will be need about 5-7 days.
5) After burning, the finished high alumina brick will be packed on pallet.

Resistance to High temperature, Resistance to erosion, resistance to abrasion;
Excellent compression strength;
Resistance to acid and alkali;
Excellent heat stability.

The high alumina bricks are widely applied to industrial furnace, glass furnace, chemical industrial furnace, utility industry furnace lining, smelting furnace, and heat insulation ventilation wall.


Physical and chemical indicators:


Al2O3 (%) ≥60 ≥70 ≥75 78-80
SIO2 (%) 32 22 20 ≥18
Fe2O3 (%) ≤1.7 ≤2.0 ≤1.8 ≤1.8
Na2O+K2O(%) <2.3 <2.0 <1.2  
Refractoriness 1790 >1770 >1790 ≥1790
refractoriness under load 0.2mpa(°C) 1450 >1510 >1520 ≥1520
Porosity (%) 22 <22 <21 20
Bulk density(g/cm3) 2.33 2.43-2.48 2.45-2.55 2.55
Cold Cushing strength (Mpa) ≥45 ≥50 ≥54 ≥60
Thermal expansion at 1000°C (%) ≤0.3 ≤0.3 ≤0.3 ≤0.3
Reheating shrinking change(%) 1500°CX24h -0.3 -0.3 -0.3 -0.3

Abrasion Resistance  Alumina Refractory Bricks For Industrial Furnace 0


Production and inspection :

Abrasion Resistance  Alumina Refractory Bricks For Industrial Furnace 1

Packaging and transportation:

Abrasion Resistance  Alumina Refractory Bricks For Industrial Furnace 2

Competitive advantage:


  • 1. Competitive Price. Make the products competitive in your market.
  1. 2. Abundant Experience. Prevent cracks and twist in bricks.
  2. 3. Different Moulds. Save mould fees for you.
  3. 4. Strict Quality Control. Meet clients’ quality requirement.
  4. 5. Large stocks. Guarantee prompt delivery.
  5. 6. Professional Packing. Avoid damage and secure the goods in transportatio