|Place of Origin:||China|
Payment & Shipping Terms:
|Minimum Order Quantity:||10Tons|
|Packaging Details:||wooden pallet with paper each layer, wrapped with thick paper and PVC film outside.|
|Payment Terms:||Western Union, T/T, L/C, D/A, D/P|
|Shape:||Brick,Block,customized||Material:||Alumina Block,calcined Bauxite|
|Refractoriness Under Load，0.2MPa，℃（≥）:||Common (1450°< Refractoriness<1450°- 1600°)||Application:||Industrial Furnaces,blast Furnace,reverberatory|
|Al2o3 Content (%):||55%-85%||Crushing Strength,≥:||45/50/60/70|
high alumina fire bricks,
fire resistant bricks
SK 34 SK 36 SK 38 High aluminum refractory fire bricks Wear Resistance Heat Resistant Bricks For Hot Blast Furnacec
High aluminum brick is a refractory material, the main component of this refractory brick is Al2O3.The Al2O3 content is higher than 90%, which is called corundum brick.Due to different resources, standards are not completely consistent.For example, in European countries, the lower limit of Al2O3 content for high alumina refractories is 42%.In China, according to the Al2O3 content in high alumina bricks are usually divided into three: Ⅰ level ─ ─ Al2O3 content > 75%.Ⅱ level ─ ─ Al2O3 content is 60 ~ 75%;Ⅲ level ─ ─ for 48 ~ 60% Al2O3 content.
High alumina brick is mainly used for lining blast furnace, hot blast furnace, electric furnace, blast furnace, reverberatory furnace and rotary kiln.In addition, high aluminum refractory brick is also widely used as open hearth regenerative lattice brick, casting system with plug, shuikou brick.
Category of Refractory Brick/Fire Brick:
a) According the made method, it can be divided into burnt brick, unburned brick, and electric smelting brick.
b) According the shape and size, it can be divided into standard brick, general brick and abnormal shape brick.
c) According the content of the Al2O3, it can be divided into fire clay brick and high alumina brick.
The production process of High Alumina Bricks can be divided into as following process:
Raw material mixing, molding, sintering, selection, packing, delivery.
1) Generally, High Alumina brick was molded by dry pressing.
2) By means of mixing the material uniformity in proportion and ageing mixture some time. Then, pour some powders into the mold and dry pressing.
3) After dry pressing, the adobe needs to be pushed in the drying kiln to stove or stay in the air to dry. This progress will need about 3-5 days.
4) After this progress, then push the adobe into the tunnel furnace or shuttle kiln to burn around 1300C. This progress will be need about 5-7 days.
5) After burning, the finished high alumina brick will be packed on pallet.
Resistance to High temperature, Resistance to erosion, resistance to abrasion;
Excellent compression strength;
Resistance to acid and alkali;
Excellent heat stability.
The high alumina bricks are widely applied to industrial furnace, glass furnace, chemical industrial furnace, utility industry furnace lining, smelting furnace, and heat insulation ventilation wall.
Physical and chemical indicators:
Refractoriness under load,
|Bulk density (g/cm3)||2.25-2.4||2.35-2.5||2.4-2.6||2.5-2.75|